What is the reason for the battery capacity of electric forklift battery?

著者：Iflowpower – Fornitore di stazioni di energia portatili

With the research and development departments, actively develop energy-saving and environmental protection products. In the industrial market, industrial equipment vehicles, electric forklifts have a certain market with convenient, simple maintenance, quiet, non-polluting, etc. Electric forklift is very suitable for use in indoor homework.

At present, there are many batteries that are mostly used in the market, which is designed to be cheap. 1. After the forklift battery is factory factory, it can be installed and used in time, causing long-term storage, long-term storage will cause self-discharge caused capacity.

Because the battery is not properly stored, it will be charged once in a period of time. 2, forklift battery positive electrode corrosion, deformation causes insufficient capacity. Forklift battery positive panel is an important factor affecting the operating life of the battery.

The capacity of the forklift battery charge and discharge cycle, especially the reduction in capacity in deep compression is closely related to the positive electrode board quality deviation. 2.1 The active material softening of the active substance is softened in the microscopic active substance, and the large pore size exceeds 0.

5 cm, which is composed of many small holes, with the discharge cycle, the surface of the active property, Forming the core and a coral structure, multiple discharge cycles use small hole aggregation, so that the large pores continue to increase, destroy the positive electrode structure, resulting in falling off the active. An important reason for these situations is caused by large current charge of the forklift battery. Preventing the occurrence of current and prevention of charge and discharge and prevent excessive or overlapping phenomenon.

2.2 The corrosion speed of the positive plate gate corrosion deformation plate grid depends on the composition of the grid alloy, but the higher the storage temperature, the faster the corrosion speed, the deeper the discharge depth, the more corrosion. 3, electric forklift battery negative plate sulfate: In normal operation, PBSO4 particles on the negative plate are small, and the discharge is easy to return to the velvet lead, but sometimes the internal cells generate difficult-to-reduced sulfate, called sulfuric acid Saline.

There are many reasons why the negative electrode is caused, such as charging after discharge, the battery is long-term shelving, causing severe self-discharge, high electrolyte concentration, long-term charging, long-term discharge, is difficult to restore Such a reduction in active substances is bound to affect the capacity of the forklift battery. Electric forklift fork fork Xiaobian reminds everyone, pay attention to counterfeit or second-hand items when purchasing forklift batteries, because some manufacturers have to earn profits by reducing product quality to raise their product quality, so far. , Look for big brands is the choice.

There is a macroporous and micropores in the microscopic substance, and the large pore size exceeds 0.5 cm, which is composed of many small holes, with the discharge cycle, the active surface shrinks, forms the core and a coral structure, more The secondary discharge cycle uses small pores to accumulate, so that the large pores are new, destroying the positive structure, causing the active object to fall off. An important reason for these conditions is that the hydropower bottle is caused by high current charge.

Preventing the occurrence of current and prevention of charge and discharge and prevent excessive or overlapping phenomenon. .